Graphite Crucible , High temperature , high power -- Good raw material .
| Model | Density | Compression Strength | Flexural Strength | Resistance | Ash | Grain Size |
| g/cm3 | Mpa | Mpa | μΩm | % | ||
| >= | >= | >= | <= | <= | ||
| 72 | 1.62 | 28 | 14 | 8 | 0.3 | 1,2,4mm |
| 72 | 1.72 | 36 | 18 | 7.5 | 0.3 | 2,0.8mm |
| 75 | 1.75 | 48 | 24 | 7.5 | 0.3 | 325mesh |
| 80 | 1.8 | 52 | 28 | 7.5 | 0.2 | 325mesh |
| 85 | 1.85 | 62 | 36 | 7 | 0.2 | 325mesh |
1. The crucible should be stocked in the dry situation
2. Carry the crucible lightly
3. Warm the crucible in the drying machine or near the
furnace. The warming temperature should be up to 500ºC.
4. The crucible should be put under the furnace month flat.
5.When put the metal into the crucible, you should take the crucible capacity as your reference. If the crucible is too full, it will be damaged by expansion.
6.The clamps shape need as that of crucible. Avoid the
concentrate stressed destroy of the crucible.
7. Clean the crucible regularly and lightly.
8. The crucible should be put in the center of the furnace and leave some distance between the crucible and furnace.
9. Turn the crucible once in one week and this will help lengthen the service life.
10. The flame should not touch the crucible directly.
11.24 hours constant use will make crucibles have longer service life.
The smelt soup in the crucible should be cleared out when the furnace stop working, in order to avoid molten soup
solidificating and will be expanded when fire to reheat, and affect the service life of crucible or even burst.
12. We suggest that about 2 months for crucible melting aluminum alloy (every week for melting copper alloy), hanging out to check whether there is something wrong in the surface, and clean furnace hearth as well as turn the crucible, this operation ishelpful to prolong the service life of crucible.
Feature |
* High temperature resistance, and the melting point is 3850±50°C, the boiling point is 4250. * Low ash content, high purity, avoiding pollution to your products. * Graphite material is easily to machine into any shapes you like. * High mechanical strength * Good sliding properties * High thermal conductivity * High thermal shock and chemical resistance * Food safety * Low wettability * High corrosion resistance and oxidation resistance * Good electrical conductivity * High density and high mechanical strength * Proper electrical conductivity |
| Usage | they are widely used in lightning protection, heat treatment, super-hard material, bearing, Non-ferrous metal casting, electro-spark processing, electronic semi-conductor, mechanical sealing, photovoltaics, glass and ceramic, automobile, carbon brush etc.. Our main products include electrode plate for surge protective device, graphite boat, graphite crucible, graphite bar, graphite mould, graphite crystallizer, mechanical sealing ring, graphite bearing, carbon bar, carbon plate, carbon disc, graphite connectors, graphite seal, carbon brush for all kinds of motors, lug plate spring etc. |
| RODUCTS | GRAPHITE MATERIAL | ISOSTATIC GRAPHITE |
| MOLDED GRAPHITE | ||
| EXTRUDED GRAPHITE | ||
| VIBRATION GRAPHITE | ||
| GRAPHITE PRODUCT | GRAPHITE TUBE | |
| GRAPHITE ROD,BLOCK,PLATE | ||
| GRAPHITE PARTS | ||
| CYLINDER OF LUBRICANT | ||
| GRAPHITE ElECTRODE | ||
| GRAPHITE CRUCIBLE |
GRAPHITE CRUCIBLE |
|
|
PRESSED CRUCIBLE |
||
|
QUARTZ CRUCIBLE |
||
| CARBON FELT/GRAPHITE FELT | CARBON FELT/GRAPHITE FELT | |
| FLEXIBLE GRAPHITE | GRAPHITE FOIL/SHEET | |
| CARBON/CARBON COMPOSITE |
CC BRAKE PADS |
|
|
CC BOARDS BLOCKS AND CYLINDERS |
||
|
CC PARTS |
||
| PRODUCTION FLOW | THE FlOW OF GRAPHITE MATERIAL AND PRODUCTS | |
| THE FLOW OF CARBON/GRAPHITE FELT |
){kind=link}