Carbon Vibrated Graphite Block for Lubricant

• Customization: Available
• Bulk Density: 1.6~1.9g/Cc Available
• Flexural Strength: 10~50MPa
• Model NO.: Vibrated graphite block
• Length: 10-3300mm
• Type: Graphite Mold
• Carbon Content: High-Carbon
• Grade: Industrial Grade
• Crystal Morphology: Compact Crystalline Graphite
• Composition: Carbon
• Forming Way: Vibrated
• Transport Package: Wooden Case
• Specification: Size as Standard or Domestic cut as your request
• Trademark: XS/other brand
• Origin: China/Worldwide
• HS Code: 3801100020
• Production Capacity: 1000ton

Product Description

Carbon vibrated graphite block for lubricant :
 

Product Name	tsk carbon vibrated  graphite block for lubricant
Application	Furnace end blocks, furnace structure and functional parts, metallurgy, casting, further machined into graphite parts
Size and Shape	Custom made according to customers requirements
Production mode	Vibrated, Extruded, Molded and  isostatic modes graphite blocks available

Carbon/Graphite Block Technical Data Parameter:
 

Type	Model	Bulk Density	Flexural Strength	Compressive Strength	Specific Resistivity	Ash Content
Extruded	YX-ER	1.55~1.60g/cc	8.0Mpa min	15.0Mpa min	8.0µΩm max	0.3% max
	YX-E1	1.63~1.70g/cc	11.0Mpa min	21.0Mpa min	6.5µΩm max	0.3% max
	YX-E2	1.66~1.73g/cc	13.0Mpa min	25.0Mpa min	6.0µΩm max	0.3% max
Vibrated	XS-VP1	1.58g/cc min	10.0Mpa min	20.0Mpa min	10µΩm max	0.3% max
	XS-VP2	1.72g/cc min	13.0Mpa min	26.0Mpa min	8.0µΩm max	0.3% max
	XS-VT1	1.68g/cc min	11.0Mpa min	23.0Mpa min	9.0µΩm max	0.3% max
	XS-VT2	1.72g/cc min	15.0Mpa min	29.0Mpa min	8.0µΩm max	0.3% max
	XS-GT1	1.69g/cc min	14.0Mpa min	30.0Mpa min	10µΩm max	0.3% max
	XS-GT2	1.72g/cc min	17.0Mpa min	34.0Mpa min	7.5µΩm max	0.3% max
Molded	XS-M23	1.78g/cc min	30.0Mpa min	60.0Mpa min	10µΩm max	0.1% max
	XS-M34	1.83g/cc min	35.0Mpa min	70.0Mpa min	10µΩm max	0.1% max
Isostatic	XS-D1	1.79g/cc min	35.0Mpa min	70.0Mpa min	10µΩm max	0.1% max
	XS-D2	1.85g/cc min	42.0Mpa min	85.0Mpa min	10µΩm max	0.1% max

Welcome your Inquiry - Xingshi Carbon