Graphite Fines Graphite Electrode Granule Synthetic Graphite Powder Artificial Graphite F. C. 98.5% 0-0.2mm, 0.1-3mm, 1-5mm

Product Description

China Xingshi Carbon Supply Graphite electrode powder/dust, grain(Granule) / Original Coke Graphitized  Synthetic graphite/Artificial Graphite 
 

Product Description

Graphite electrode grain powder/ Synthetic graphite/ Artificial Graphite Fines  98.5 % min, 99%min 

1. Graphite electrode powder: As the name suggests, it is produced from graphite electrodes and is a by-product of the production of graphite electrodes.

    Graphite electrode scrap is made of high-quality graphite electrode lower corner materials and cutting materials our factory from large domestic graphite electrode manufacturers through manual cleaning, crushing, screening and selection. It is a high-quality carburizing agent used in the steel-making and casting industries. It has obvious carburizing effect, high absorption rate and high dissolution rate, which can significantly improve the toughness and malleability of steel and iron castings

2.  Graphite Electrode scrap for the Steel and Metal Industry as Carbon Raiser/Carbon additive

3.  We also have other synthetic graphite powder, like Crucible, Block and other graphite scrap to produce the graphite fines. 
 

 

Product Parameters

Graphite Electrode Scraps - Synthetic Graphite powder
Items	1#	2#	3#
Fixed carbon	99%min	98.5%min	98%min
Sulfur	0.045%max	0.045%max	0.045%max
Ash	0.5%max	0.8%max	1%max
Volatile matter	0.5%max	0.7%max	1%max
Moisture	0.5%max	0.5%max	0.5%max
Size	0-1mm , 1-5mm or 1-4mm,95% min , Customized

    ** Other Grain size,   Accepting customization, starting from scratch, with lower prices!

There are usually two types of graphite electrode carburizers sold in the market: one is waste generated during the machining of electrodes, and the other is the crushed parts of graphite electrodes after use.

Product Display

 

 

 

 

Application

 

1. Related Completely Graphite electrode Rod: Make small graphite workpieces( Use big pieces of graphite electrode , to do Crucible, Small graphite machine parts.

2. For crushing and carburizing(  High quality and Best Efficiency Carbon Raiser . Graphitized Carburante , Carbon additive , Synthetic graphite granular powder for Steel and Other metal Melting Industry )

3. Crush to make conductive material  - ( Customized Pieces)

Others

1. Carbon Raiser / Carburizing agent is mostly used in induction furnace, but the specific use is also different according to the process requirements

(1) When using a carburizing agent in medium frequency electric furnace smelting, it can be added to the lower part of the electric furnace according to the proportion or carbon demand, and the recovery rate can reach more than 95%


(2) If the carbon content is not enough to adjust the carbon content, clean the slag first, and then add carburizing agent. The carbon is dissolved and absorbed through liquid iron heating, electromagnetic stirring or manual stirring, and the recovery rate can be about 90%. If the low-temperature carburizing process is adopted, that is, only part of the furnace charge is melted, and the molten iron temperature is low, all carburizing agents are added to the molten iron at one time, and the solid furnace charge is used at the same time Press it into molten iron to prevent it from exposing the surface of molten iron. This method can increase the carbon content of molten iron by more than 1.0%.


2: Carburization outside furnace


(1) Spraying graphite powder in package


When graphite powder is selected as carburizing agent, the blowing amount is 40kg / T, which is expected to increase the carbon content of molten iron from 2% to 3%. With the gradual increase of carbon content of molten iron, the carbon utilization rate decreases, and the temperature of molten iron is 1600c. After carburization, the average temperature is 1299c. Graphite powder is used for carburization. Generally, nitrogen is used as the carrier. However, under industrial production conditions, it is more convenient to use compressed air, and the oxygen combustion in the compressed air produces Co. the heat of chemical reaction can compensate for partial cooling, and the reduction atmosphere of CO is conducive to improving the carburization effect.


(2) Use carburizing( Carbon raiser ) agent during tapping


100-300 mesh graphite powder carburizing agent can be put into the package, or washed in with the flow from the rizer D tapping tank. After the liquid iron is discharged, it can be fully stirred to dissolve and absorb the liquid carbon as much as possible, and the carbon recovery rate is about 50%.

The Graphite electrode scrap is one of the Best efficiency graphite carbon raiser.