• Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
  • Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
  • Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
  • Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
  • Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
  • Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite

Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite

Type: Graphite Electrodes
Composition: Fixed Carbon
Carbon Content: High-Carbon
Grade: Industrial Grade
Forming Way: Extruded Graphite
Crystal Morphology: Artificial Graphite
Samples:
US$ 50/kg 1 kg(Min.Order)
| Request Sample
Customization:

Contact Supplier

Diamond Member Since 2019

Suppliers with verified business licenses

Group Corporation

Basic Info.

Model NO.
graphite fines
Size Popular
1-5mm
Fixed Carbon
98.5% Min
Ash
0.5% Max
Moisture
0.5% Max
Transport Package
25kg Bags or Jumbo Bag
Specification
Customized
Trademark
XS
Origin
China
HS Code
3801100090
Production Capacity
8000tons/Month

Product Description

Artificial Graphite Fines  98.5 % min  , Low sulphur


ll Graphite Electrode scrap for the Steel and Metal  Inudstry  as Carbon Raiser ,Export to India , Iran Egypt ...

 

1. Introduction 

 

Graphite electrode scrap is made of high-quality graphite electrode lower corner materials and cutting materials our factory from large domestic graphite electrode manufacturers through manual cleaning, crushing, screening and selection. It is a high-quality carburizing agent used in steel-making and casting industries. It has obvious carburizing effect, high absorption rate and high dissolution rate, which can significantly improve the toughness and malleability of steel and iron castings.

 

 

2. Best- selling Parameters :

 

 

 Graphite Electrode Scraps - Synthetic Graphite powder 

 Items 

1#

2#

3#

 Fixed carbon

99%min

98.5%min

98%min

 Sulfur

0.045%max

0.045%max

0.045%max

 

 Ash

0.5%max

0.8%max

1%max

 

 Volatile matter

0.5%max

0.7%max

1%max

 Moisture

0.5%max

0.5%max

0.5%max

 Size

0-1mm , 1-5mm or 1-4mm,95% min , Customized



Products Photos :

Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite

USAGE :

1. Make small graphite workpieces( Use big pieces of graphite electrode , to do Crucible , Small graphite parts )

2. For crushing and carburizing(  High quality and Best Efficiency Carbon Raiser . Graphitized Carburante , Carbon additive , Synthetic graphite granular powder for Steel and Other metal Melting Industry )

3. Crush to make conductive material  - ( Customized Pieces)

Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial GraphiteLow Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite



Carbon Raiser / Carburizing agent is mostly used in induction furnace, but the specific use is also different according to the process requirements


(1) When using carburizing agent in medium frequency electric furnace smelting, it can be added to the lower part of the electric furnace according to the proportion or carbon demand, and the recovery rate can reach more than 95%


(2) If the carbon content is not enough to adjust the carbon content, clean the slag first, and then add carburizing agent. The carbon is dissolved and absorbed through liquid iron heating, electromagnetic stirring or manual stirring, and the recovery rate can be about 90%. If the low-temperature carburizing process is adopted, that is, only part of the furnace charge is melted, and the molten iron temperature is low, all carburizing agents are added to the molten iron at one time, and the solid furnace charge is used at the same time Press it into molten iron to prevent it from exposing the surface of molten iron. This method can increase the carbon content of molten iron by more than 1.0%.


2: Carburization outside furnace


(1) Spraying graphite powder in package


When graphite powder is selected as carburizing agent, the blowing amount is 40kg / T, which is expected to increase the carbon content of molten iron from 2% to 3%. With the gradual increase of carbon content of molten iron, the carbon utilization rate decreases, and the temperature of molten iron is 1600c. After carburization, the average temperature is 1299c. Graphite powder is used for carburization. Generally, nitrogen is used as the carrier. However, under industrial production conditions, it is more convenient to use compressed air, and the oxygen combustion in the compressed air produces Co. the heat of chemical reaction can compensate for partial cooling, and the reduction atmosphere of CO is conducive to improving the carburization effect.


(2) Use carburizing( Carbon raiser ) agent during tapping


100-300 mesh graphite powder carburizing agent can be put into the package, or washed in with the flow from the rizer D tapping tank. After the liquid iron is discharged, it can be fully stirred to dissolve and absorb the liquid carbon as much as possible, and the carbon recovery rate is about 50%.

The Graphite electrode scrap is one of Best efficiency graphite carbon raiser .

Low Sulfur Low Nitrogen Graphite Fines Carbon Raiser|Artificial Graphite
 

Send your message to this supplier

*From:
*To:
avatar Mrs. Zhang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Contact Supplier

Diamond Member Since 2019

Suppliers with verified business licenses

Group Corporation
Registered Capital
5000000 RMB
Plant Area
101~500 square meters